Next Nylon 6 Prime Series NMS1-01 S.GY.
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9plg9E_Next-Nylon-6-Prime-Series-NMS1-01-S-GY-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 MOS2 Filled Steel Grey compound Product Applications It is the ideal for dynamic bearing application, event at elevated temperature ex. gears, sheaves, sprockets, custom parts etc Benefits Excellent wear resistance, Self lubricated and Low friction characteristics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.15 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.85 | -- | % | |
| Across Flow | 0.85 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.60 | -- | % | |
| Saturation 1 | 7.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2700 | 1900 | MPa | ASTM D638 |
| Tensile Strength | 75.0 | 55.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | > 40 | % | ASTM D638 |
| Flexural Modulus | 3400 | 2700 | MPa | ASTM D790 |
| Flexural Strength | 110 | 85.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | 69 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 180 | -- | °C | |
| 1.8 MPa, Unannealed | 95.0 | -- | °C | |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| CLTE - Flow | 9.0E-5 | -- | cm/cm/°C | ASTM E831 |
| Thermal Conductivity | 0.30 | -- | W/m/K | ASTM D5930 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 24 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Talcoprene® OC3030 CM GRIGIO313 | SO.F.TER. SPA | PP, Unspecified | Talcoprene® |
| VALOX™ ENH4560 resin | SABIC Innovative Plastics Europe | PBT | VALOX™ |
| Evoprene™ G 3294 | AlphaGary | SEBS | Evoprene™ G |
| Monprene® SP-19985 XRD2 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| LNP™ LUBRICOMP™ RFL36L compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |