Ferro PP TPP40AJ02HB
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9oPwes_Ferro-PP-TPP40AJ02HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP TPP40AJ02HB is a polypropylene homopolymer (PP Homopoly) material, which contains 40% talc filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. The main characteristics of Ferro PP TPP40AJ02HB are: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.90 | % | ASTM D955 |
| Transverse flow | 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 2820 | MPa | ASTM D790 |
| Tangent : 23°C | 4310 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 50.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 240 | J/m | ASTM D256 |
| Dart Drop Impact | 0.904 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 138 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 85.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Filler Content, ASTM D2584: 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ PTFE Compound TF 6105N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| BITONER® BT-2110 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Clear Cote™ POLY-U-FOAM™ 4 lb Urethane Foam System | Club Kit, Inc. | PUR, Unspecified | Clear Cote™ |
| LUVOCOM® 80-8072 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Sylvin 86051-65DFU Clear | Sylvin Technologies Incorporated | PVC, Semi-Rigid | Sylvin |