LNP™ LUBRICOMP™ RAP22 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9nGuwF_LNP-LUBRICOMP-RAP22-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RAP22 is a compound based on Nylon 66 resin containing 10% Aramid, 10% PTFE/Silicone. Added feature of this grade includes: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RAL-4522 Product reorder name: RAP22 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.71 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.1 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3390 | MPa | ASTM D638 |
| -- | 3430 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 51.9 | MPa | ASTM D638 |
| Yield | 71.0 | MPa | ISO 527-2/5 |
| Break 3 | 49.1 | MPa | ASTM D638 |
| Break | 71.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.7 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/5 |
| Break 5 | 2.7 | % | ASTM D638 |
| Break | 6.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3260 | MPa | ASTM D790 |
| -- 7 | 3260 | MPa | ISO 178 |
| Flexural Stress | 103 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.38 | ||
| vs. Itself - Static | 0.26 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | -0.300 to -0.200 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 23.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 30 | J/m | ASTM D256 |
| 23°C 8 | 3.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 340 | J/m | ASTM D4812 |
| 23°C 9 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 4.70 | J | ASTM D3763 |
| -- | 0.900 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 224 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 189 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 100 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 4.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.7E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 2405 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Tecnoflon® P 459 | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| CERTENE™ 780 | Muehlstein | ABS | CERTENE™ |
| LNP™ THERMOCOMP™ MFB63 compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ THERMOCOMP™ |
| Jam HD-7260 (I3) | Jam Petrochemical Company | HDPE | Jam |