INSULCAST® RTVS 11
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® RTVS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9l68Dk_INSULCAST-RTVS-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RTVS 11 is a low viscosity, multi-purpose compound, designed for use as a potting, encapsulating, sealing and mold making material. Due to its excellent electrical properties, the RTVS 11 is used extensively as a high voltage potting compound, as well as an encapsulating compound for delicate circuitry. The RTVS 11 can be used with various curing agents, thus varying pot life, cure time, mix ratios and cure conditions. (See RTVS Catalyst Selector Guide). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 3.45 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 150 | % | ASTM D412 |
| Tear Strength 1 | 3.50 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 2.5E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.31 | W/m/K | |
| Service Temperature | -55 to 204 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mixing Ratio - by weight 2 | 0.10 to 0.50 | % |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear Shrinkage | 0.20 to 0.50 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.020 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shelf Life (25°C) | 26 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | White | ||
| Density | 1.18 | g/cm³ | |
| Viscosity | 12 | Pa·s | ASTM D2393 |
| Curing Time (25°C) | 24 | hr | |
| Pot Life 3(25°C) | 15 to 120 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| 2 . | w/CAT-2 |
| 3 . | varies with % of CAT-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAISOX 9003 | Formosa Plastics Corporation | HDPE | TAISOX |
| Niretan A F20 AE/V2 | Soredi S.p.a. | Nylon 66 | Niretan A |
| Novalloy-B B2504 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| Diakon® Frost 952 51 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| LNP™ STAT-KON™ DX91077 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |