Romiloy® 5730/01
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | ROMIRA GmbH |
| Trademark: | Romiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9idZAm_Romiloy573001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Romiloy®5730/01 is a polycarbonate polybutene terephthalate (PC PBT) material,. This product is available in Europe, and the processing method is injection molding. Romiloy®The main features of 5730/01 are:
|
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 0.50 - 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | MPa | ISO 527-2/1 |
| Tensile Stress (23°C) | 49.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1950 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 40 | kJ/m² | ISO 179/1eA |
| 23°C | 50 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 114 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ AS-1000 AS | PolyOne Corporation | ABS | Stat-Tech™ |
| VENELENE® 11U4 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| HANWHA EVA 1528 | Hanwha Chemical | EVA | HANWHA EVA |
| KRATON® D1114 P | Kraton Polymers LLC | SIS | KRATON® |
| Optema™ TC 220 Molding | ExxonMobil Chemical | EMA | Optema™ |