Tritan™ MP200
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9iVzur_TritanMP200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Tritan MP200 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Film and sheet manufactured from this new-generation copolyester can be thermoformed with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan MP200 copolyester is suitable for use with most forms of sterilization including radiation and ethylene oxide. It is NOT suitable for autoclave/steam sterilization. Eastman Tritan MP200 copolyester has been formulated for use in medical film, sheet, and packaging applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ASTM D1505 |
| Water Absorption (24 hr) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Wear resistance (23°C) 1 | 20% Haze | ASTM D1044 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Permeability (23°C, 254.0 µm) | 210 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| PPT Tear Resistance | ASTM D2582 | ||
| MD : 23°C, 254.0 µm | 40 | N | ASTM D2582 |
| TD : 23°C, 254.0 µm | 40 | N | ASTM D2582 |
| Tear Propagation Resistance | ASTM D1938 | ||
| MD, Split Tear Method : 23°C, 254.0 µm | 310 | gf | ASTM D1938 |
| TD, Split Tear Method : 23°C, 254.0 µm | 200 | gf | ASTM D1938 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance 2 | 89 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Energy | ASTM D5946 | ||
| Dispersive : 23°C | 39 | dyne/cm | ASTM D5946 |
| Polar : 23°C | 8 | dyne/cm | ASTM D5946 |
| Total : 23°C | 47 | dyne/cm | ASTM D5946 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 250 | µm | ASTM D374 |
| Elastic Modulus - MD (250 µm) | 1500 | MPa | ASTM D882 |
| Elastic Modulus - TD (250 µm) | 1400 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 250 µm | 43.0 | MPa | ASTM D882 |
| TD : Yield, 250 µm | 41.0 | MPa | ASTM D882 |
| MD : Break, 250 µm | 57.0 | MPa | ASTM D882 |
| TD : Break, 250 µm | 42.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 250 µm | 8.0 | % | ASTM D882 |
| TD : Yield, 250 µm | 8.0 | % | ASTM D882 |
| MD : Break, 250 µm | 110 | % | ASTM D882 |
| TD : Break, 250 µm | 120 | % | ASTM D882 |
| Dart Drop Impact 3 | ASTM D1709A | ||
| -30°C, 250 µm | 850 | g | ASTM D1709A |
| -18°C, 250 µm | 830 | g | ASTM D1709A |
| 23°C, 250 µm | 830 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 250 µm | 380 | g | ASTM D1922 |
| TD : 250 µm | 430 | g | ASTM D1922 |
| Trouser Tear Resistance 4 | ISO 6383-1 | ||
| MD : 250 µm | 10.0 | N/mm | ISO 6383-1 |
| TD : 250 µm | 9.00 | N/mm | ISO 6383-1 |
| Oxygen Permeability (23°C, 250 µm) | 44 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 23°C, 100% RH, 250 µm | 4.0 | g/m²/24 hr | ASTM F1249 |
| 38°C, 100% RH, 250 µm | 10 | g/m²/24 hr | ASTM F1249 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact (23°C, 0.254 mm, Total Energy) | 4.50 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 119 | °C | DSC |
| CLTE - Flow (23°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | DSC | ||
| 60°C | 1700 | J/kg/°C | DSC |
| 100°C | 1900 | J/kg/°C | DSC |
| 150°C | 2300 | J/kg/°C | DSC |
| 200°C | 2400 | J/kg/°C | DSC |
| 250°C | 2600 | J/kg/°C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 254 µm) | 158 | ASTM D2457 | |
| Refractive Index | 1.540 | ASTM D542 | |
| Transmittance (Total, 254 µm) | 93.0 | % | ASTM D1003 |
| Haze (254 µm) | 0.80 | % | ASTM D1003 |
| Yellowness Index (0.254 mm) | 0.50 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 25 cycles |
| 2 . | UV/Vis Spectro, 380 nm |
| 3 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 4 . | 200 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 330B FR | RTP Company | PC | RTP |
| Xuchuan XCS-2086B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| ADENE OTJB | A.D. Compound spa | PP Homopolymer | ADENE |
| Kingfa HC-110 | Kingfa | ABS | Kingfa |
| Sylvin 9053-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |