| The plasticized and impact modified PA12 grade UBESTA 3030 JI14L is equipped with a special low migration plasticizer offering high dimensional stability. The grade is stabilized against heat and weatherability. It is designed for high burst pressure performance at elevated temperatures as for brake systems in trucks with operating pressures of 12.5 bar. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.5 | % | ISO 294-4 |
| Flow direction | 0.70 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 69 | ISO 2039-2 | |
| Durometer Hardness (Shore D) | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 19 | % | ISO 527-2 |
| Fracture | 200 | % | ISO 527-2 |
| Flexural Modulus | 700 | MPa | ISO 178 |
| Flexural Stress | 28.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, complete fracture | 5.0 | kJ/m² | ISO 179/1eA |
| 23°C, local fracture | 90 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 96.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 45.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 175 | °C | ISO 3146 |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Tensile Strain at Break, ISO 527: >200%Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 7 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® MP635662 | LyondellBasell Industries | LLDPE | Microthene® |
| TAIRIPRO K4715 | Formosa Plastics Corporation | PP Random Copolymer | TAIRIPRO |
| Ultraform® N 2320 003 UNC Q600 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| Daplen™ EE103AEB | Borealis AG | TPO | Daplen™ |
| DURACON® JW-03 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |