TUFLIN™ HS-7029 NT 7
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | TUFLIN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9iMCgG_TUFLIN-HS-7029-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TUFLIN™ HS-7029 NT 7 Linear Low Density Polyethylene Resin is an ethylene-hexene copolymer designed for cast and blown film applications such as trash bags, industrial can liners, heavy duty shipping sacks and retail bags. Films extruded with HS-7029 exhibit superb toughness, high tensile strength and elongation, excellent tear and puncture resistance, and are readily heat sealable. Applications: Trash bags, industrial can liners, heavy duty shipping sacks and retail bags Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | Internal method |
| Film Puncture Energy | 3.39 | J | Internal method |
| Film Puncture Force | 44.5 | N | Internal method |
| Film Puncture Resistance | 18.6 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 82.7 | J/cm³ | ASTM D882 |
| TD | 91.0 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 221 | MPa | ASTM D882 |
| 2% secant, MD | 200 | MPa | ASTM D882 |
| 1% secant, TD | 303 | MPa | ASTM D882 |
| 2% secant, TD | 255 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 10.3 | MPa | ASTM D882 |
| TD : Yield | 11.7 | MPa | ASTM D882 |
| MD : Fracture | 33.8 | MPa | ASTM D882 |
| TD : Fracture | 29.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 500 | % | ASTM D882 |
| TD : Fracture | 600 | % | ASTM D882 |
| Dart Drop Impact | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 350 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 22 | ASTM D2457 | |
| Haze | 28 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions for 1 mil monolayer blown film at 100% Die Diameter: 8 in. Screw Type: DSB II Die Gap: 70 mil Melt Temperature: 405 °F Output: 12 lb/hr/in. of die circumference Screw Size: 3.5 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 39 rpm Frost Line Height: 52 in. |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT7012-707UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Staramide RF00AES | Eurostar Engineering Plastics | Nylon 66/6 | Staramide |
| Huafon JF-S-M8090 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| SQUARE® LIM3919-30A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| Durethan® BKV 50 H3.0 000000 | LANXESS GmbH | Nylon 6 | Durethan® |