SABIC® PP PHC31
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9hgtSp_SABIC-PP-PHC31.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade combines high stiffness with good impact strength. Its excellent flow properties and narrow molecular weight distribution allows fast cycle-times and injection moulding of articles demanding low warpage and high dimensional stability. Typical applications are pails, containers, crates & boxes and automotive components. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 92 | ASTM D785 | |
| Shore Hardness (Shore D) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1350 | MPa | ASTM D638 |
| -- | 1300 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 25.0 | MPa | ASTM D638 |
| Yield | 25.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 5.0 | kJ/m² | |
| 0°C | 8.0 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Notched Izod Impact | |||
| -20°C | 50 | J/m | ASTM D256A |
| 0°C | 75 | J/m | ASTM D256A |
| 23°C | 100 | J/m | ASTM D256A |
| -20°C | 5.0 | kJ/m² | ISO 180/1A |
| 0°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 80.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525 6 |
| -- | 76.0 | °C | ASTM D1525 7 |
| -- | 149 | °C | ISO 306/A120 |
| -- | 74.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® PA540N | Guangdong Silver Age Sci & Tech. Co., Ltd | Nylon 6 | SILVER® |
| AvaSpire® AV-722 CF30 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| Ferro PP TPP20AA10NA | Ferro Corporation | PP, Unspecified | Ferro PP |
| Hylex® P1010G10FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| Flexirene® FG 33 U | Versalis S.p.A. | LLDPE | Flexirene® |