RAMOFIN PPC361T4
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9hGgHs_RAMOFIN-PPC361T4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% MINERAL FILLED, HEAT RESISTANT POLYPROPYLENE FOR INJECTION MOULDINDG APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.80 - 1.2 | % | ASTM D955 |
| -- | 0.80 - 1.2 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 17.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1900 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 40.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 150 | J/m | ASTM D256 |
| 23°C | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 105 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | 120 | °C | |
| Maximum Continuous Use Temperature | 110 | °C | |
| Melting Temperature | 165 | °C | ISO 11357-3, ASTM D3418 |
| Thermal Conductivity | 140 | W/m/K | ASTM C177, DIN 52612 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 225 | °C | |
| Front Temperature | 205 - 230 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 102 GB 15 | RTP Company | PP Homopolymer | RTP |
| TAIRILAC WG1700 | Formosa Plastics Corporation | ASA | TAIRILAC |
| Axiall PVC 8740 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Evermore PUR SS-302P | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| POCAN® B 1205 XF 000000 | LANXESS Asia/Pacific | PBT | POCAN® |