Ateva® 2830A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9gaaXO_Ateva-2830A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for hot melt coating and adhesive applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 150 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 28.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 73 | ||
| Shore D | 19 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 4.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 810 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 15.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 68.0 | °C | ASTM D3418 |
| Ring and Ball Softening Point | 91 | °C | ASTM E28 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA612 GYELVN | Shandong Guangyin New Materials Co., Ltd. | Nylon 612 | Shandong PA612 |
| Adstif EA640G | LyondellBasell Industries | PP Impact Copolymer | Adstif |
| ArgoMedPLUS® 18411 | Argotec LLC | TPU, Unspecified | ArgoMedPLUS® |
| Fainplast PVC MPH 69/H | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Excelprene® 55F | S&E Specialty Polymers, LLC | TPE | Excelprene® |