NEONIT® SK80 L8G
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | SBHPP |
| Trademark: | NEONIT® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9gKG00_NEONITSK80L8G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NEONIT® SK80 L8G is a long glass fiber reinforced epoxy molding compound with excellent long term property retention over a wide temperature range and climate conditions. It is particularly suited for over molding and manufacturing of large commutators. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.79 | g/cm³ | ISO 1183 |
| Apparent Density | 0.59 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.11 | % | ISO 2577 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.050 | % | ISO 62 |
| Post Shrinkage | -0.020 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19000 | MPa | ISO 527-2 |
| Tensile Stress | 119 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.70 | % | ISO 527-2 |
| Flexural Modulus | 17000 | MPa | ISO 178 |
| Flexural Stress | 255 | MPa | ISO 178 |
| Compressive Stress | 265 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 54 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 195 | °C | TMA |
| Linear thermal expansion coefficient | TMA | ||
| Flow | 1.0E-5 | cm/cm/°C | TMA |
| Lateral | 5.7E-5 | cm/cm/°C | TMA |
| Thermal Conductivity | 0.49 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 29 | kV/mm | IEC 60243-1 |
| Dissipation Factor (23°C, 1 MHz) | 0.019 | IEC 60250 | |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8878-80 White 1455 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| WELLAMID Nylon 6000 SCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| XANTAR® G2F 23 R | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| DINALON® B1S25 G30 | Grupo Repol | Nylon 6 | DINALON® |
| Extir® CM Giotto 5 AE | Versalis S.p.A. | PS (EPS) | Extir® |