CP PRYME® ABS A100HR-67
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Chase Plastics Services Inc. |
| Trademark: | CP PRYME® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9fyygW_CPPRYMEABSA100HR67.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled Prime ABS, Heat Resistant, Injection Molding Grade |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 47.1 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20mm | > 5.0 | % | ASTM D638 |
| Fracture, 3.20mm | 20 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 78 | J/m | ASTM D256 |
| -30°C, 6.40 mm | 69 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 160 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 116 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 107 | °C | ASTM D648 |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.5E+3 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 33 | kV/mm | ASTM D149 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® H35C | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Sindustris POM HI511 | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| TES J-1200/30 | Techmer Engineered Solutions | ABS | TES |
| V-TEM 80 | S&E Polymer Solutions, Inc. | TPE | V-TEM |
| GLAMIDE® TY-102ND | TOYOBO America, Inc. | Nylon 6 Elast | GLAMIDE® |