Hostacom M2 N03 L356521
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9efG0M_HostacomM2N03L356521.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom M2 N03 L356521 is a mineral filled PP homopolymer, with low melt flow rate. Product is UL listed. This grade is not intended for medical, pharmaceutical, food and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 8.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 9.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 6.0 | % | ISO 527-2 |
| Flexural Modulus 1(23°C) | 2800 | MPa | ISO 178/A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SWANCOR Epoxy 900 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| TARODUR 100 G3 | Taro Plast S.p.A. | ABS | TARODUR |
| TOTAL Polyethylene MDPE 3802 (Blow Molding) | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| New-prene™ 9150N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Bergadur™ PBT-GL30 BK007 | PolyOne Corporation | PBT | Bergadur™ |