TECHNYL® AZ 536 V20 BLACK
| Category: | PPE+Nylon 66 , Polyphenylene Ether + PA 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9duZWZ_TECHNYLAZ536V20BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® AZ 536 V20 Black is a polyamide blend of polamide 66 and polyphenyl ethers (PPE), reinforced with 20% of glass fiber, for extrusion. This grade offers a reduced thermal conductivity in comparison to commonly used materials such as polyamide 66 glass fiber reinforced. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 1.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 7180 | -- | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield, 23°C | 122 | -- | MPa | ISO 527-2/1A |
| Fracture, 23°C | 122 | -- | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | 2.4 | -- | % | ISO 527-2 |
| Fracture, 23°C | 2.4 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5020 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 157 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.4 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 42 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 6.2 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 236 | -- | °C | ISO 75-2/Bf |
| Melting Temperature | 262 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Mold Temperature | 270 - 290 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -35°C. Recommended time 8hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HHR102 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Delta N66-100CL | Delta Polymers | Nylon 66 | Delta |
| Kazan HDPE PEBO-285D | Kazanorgsintez Joint Stock Company | HDPE | Kazan HDPE |
| Plenco 07200 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |
| Kepital® F20-03M | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |