DENYL 66 4022
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | DENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9dgX5e_DENYL-66-4022.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 40% mineral filled, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.44 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.80 | -- | % | |
| Across Flow | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2200 | -- | MPa | ASTM D638 |
| Tensile Strength (Yield) | 40.0 | -- | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | -- | % | ASTM D638 |
| Flexural Modulus | -- | 3400 | MPa | ASTM D790, ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 6.0 | -- | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 50 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | -- | °C | ASTM D648A |
| Vicat Softening Temperature | 235 | -- | °C | ASTM D1525 1 |
| RTI Elec | 120 | -- | °C | UL 746 |
| RTI Imp | 120 | -- | °C | UL 746 |
| RTI Str | 120 | -- | °C | UL 746 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 100 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2920-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NuSil CV4-2289-1 | NuSil Technology | Silicone | NuSil |
| DOMAMID® 66STZX | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Hifax TYC 258X | LyondellBasell Industries | PP Copolymer | Hifax |
| LUVOCOM® 1105-8344/EM/GY | Lehmann & Voss & Co. | PEEK | LUVOCOM® |