Retpol® 3013 HS UV3
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9dFkNf_Retpol-3013-HS-UV3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extron 3013 HS UV3 is a 20% glass fibre reinforced coupled polypropylene compound. It is a medium flow injection moulding grade developed for components requiring high rigidity, good impact strength, high heat deflection temperatures and improved creep resistance. It is UV stabilised to withstand long term outdoor weathering. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 110 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 77 | ||
| Shore D, 15 sec, 3.00 mm | 72 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 72.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 3960 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 70 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 470 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 158 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 144 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 4.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800 B-65A HF UV | RTP Company | TPV | RTP |
| RAMOFIN PPH316G4 | Polyram Ram-On Industries | PP Homopolymer | RAMOFIN |
| MTEGRITY™ PP Homopolymer PP410 | M. Holland Company | PP Homopolymer | MTEGRITY™ PP Homopolymer |
| Mylar® EL-21 (900 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| ENFLEX V1040D | ENPLAST Americas, a Ravago Group Company | TPV | ENFLEX |