Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ UX06427 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9cnuum_LNP-LUBRICOMP-UX06427-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UX06427 is a compound based on PPA containing 30% Carbon Fiber, 15% PTFE. Added features of this grade include: Heat Stabilized, Hot Water Moldable, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound UCL-4036 A HS HW Product reorder name: UX06427 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.42 | g/cm³ | ASTM D792 |
| -- | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.060 to 0.090 | % | |
| Across Flow : 24 hr | 0.60 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 25200 | MPa | ASTM D638 |
| -- | 22800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 224 | MPa | ASTM D638 |
| Yield | 227 | MPa | ISO 527-2/5 |
| Break 3 | 224 | MPa | ASTM D638 |
| Break | 227 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 1.3 | % | ASTM D638 |
| Yield | 1.3 | % | ISO 527-2/5 |
| Break 5 | 1.3 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 17200 | MPa | ASTM D790 |
| -- 7 | 19600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 309 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 311 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 311 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.34 | ||
| vs. Itself - Static | 0.33 | ||
| Wear Factor - Washer | 26.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Minimum Moisture Content | 0.030 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 650 | J/m | ASTM D4812 |
| 23°C 11 | 40 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 2.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 296 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 298 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 284 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 284 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 4.0 | hr | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styropor® F 315 E | BASF Corporation | PS (EPS) | Styropor® |
| Nanguang TPU S-95AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| BLUESTAR® PBT 403G-M20 | Nantong Zhonglan Engineering Plastics Co., Ltd. | PBT | BLUESTAR® |
| Carbotex KV-75FD | Kotec Corporation | PC | Carbotex |
| Petrothene® NA420234 | LyondellBasell Industries | LDPE+EVA | Petrothene® |