LUVOCOM® 1-9158

Category: Nylon 66 , Polyamide 66
Manufacturer: LEHVOSS Group
Trademark: LUVOCOM®
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: 9cY9P3_LUVOCOM19158.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
LUVOCOM®1-9158 is a polyamide 66 (nylon 66) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1-9158 are:
  • Conductivity
  • anti-warping
  • Good stiffness

Typical application areas include:
  • textile/fiber
  • engineering/industrial accessories
  • Automotive Industry
  • business/office supplies
General Information
Features
  • Conductivity
  • Heat conduction
  • Low warpage
  • Rigid, good
  • Static conduction
  • Good strength
Uses
  • Textile applications
  • Engineering accessories
  • Application in Automobile Field
  • Business equipment
Appearance
  • Natural color
PhysicalNominal ValueUnitTest Method
Density 1.45g/cm³ISO 1183
Melt Mass-Flow Rate (MFR) (300°C/10.0 kg)10g/10 minISO 1133
Molding Shrinkage 0.60 - 1.3%DIN 16901
Water Absorption (23°C, 24 hr)< 1.3%
MechanicalNominal ValueUnitTest Method
Tensile Modulus 8000MPaISO 527-2
Tensile Stress (Break)40.0MPaISO 527-2
Tensile Strain (Yield)0.70%ISO 527-2
Flexural Modulus 7000MPaISO 178
Flexural Stress 55.0MPaISO 178
Flexural Strain at Flexural Strength 0.90%ISO 178
ThermalNominal ValueUnitTest Method
Maximum operating temperature- Short Term 140°C
ElectricalNominal ValueUnitTest Method
Insulation Resistance 1.0E+2 - 1.0E+4ohmsIEC 60167
ThermalNominal ValueUnitTest Method
Continuous Use Temperature 100°CUL 746B
Thermal Conductivity 128W/m/K
ElectricalNominal ValueUnitTest Method
Surface Resistivity < 1.0E+4ohmsIEC 60093
InjectionNominal ValueUnit
Drying Temperature
    Hot air dryer, A 75°C
    Vacuum dryer, B 105°C
Drying Time
    Hot air dryer, A 6.0 - 16hr
    Vacuum dryer, B 4.0 - 6.0hr
Rear Temperature 290 - 310°C
Middle Temperature 290 - 310°C
Front Temperature 290 - 310°C
Nozzle Temperature 280 - 300°C
Processing (Melt) Temp 290°C
Mold Temperature 90 - 120°C
Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Note Message
1 .Hot-Disk, 60x60x3 mm
Resin Grade Manufacturer Category Trademark
SABIC® PPcompound 7500 Saudi Basic Industries Corporation (SABIC) PP, Unspecified SABIC® PPcompound
YUCLAIR® FN410 SK Global Chemical LLDPE YUCLAIR®
Amodel® AFA-6133 V0 Z Solvay Specialty Polymers PPA Amodel®
KOPLA PA66 KDR1026 KOPLA Co., Ltd. Nylon 66 KOPLA PA66
Pearlthane® ECO D12T80 Lubrizol Advanced Materials, Inc. TPU, Unspecified Pearlthane® ECO