Nymax™ GF 600 A 33 Natural
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9cWUVS_Nymax-GF-600-A-33-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nymaxm of glass fiber reinforced nylon 6 polymer®GF600 series products are specially designed for high rigidity, tensile strength and toughness applications, and their surface appearance is improved compared with nylon 6/6 polymer. According to the required stiffness characteristics, these materials have a variety of strength levels to choose from and are easy to process in most standard thermoplastic processing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527 |
| Tensile Strength | |||
| Yield 1 | 165 | MPa | ASTM D638 |
| Fracture | 180 | MPa | ISO 527 |
| Tensile Elongation | |||
| Yield 2 | 4.0 | % | ASTM D638 |
| Fracture | 12 | % | ISO 527 |
| Flexural Modulus | |||
| -- | 9310 | MPa | ISO 178 |
| -- | 8700 | MPa | ASTM D790 |
| Flexural Strength | 260 | MPa | ISO 178, ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 130 | J/m | ASTM D256A |
| Local fracture | 15 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, annealed, 3.18mm | 204 | °C | ASTM D648 |
| 1.8 MPa, annealed | 202 | °C | ISO 75-2/A |
| Melting Temperature | 220 | °C | ASTM D789 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| 模制试验条：模制时干燥 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 48.9 - 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ X444H | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Elexar® EL-1934A | Teknor Apex Company | TPE | Elexar® |
| HIFOR Xtreme® SC74859 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| Kumho SSBR SOL-5250H | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| MAJ'ECO EFRHWP304R - 1199 | AD majoris | PP, Unspecified | MAJ'ECO |