DURANEX® C5315N
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | DURANEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9cUaXe_DURANEX-C5315N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Better Surface Appearance, Higher Gloss, HB, GF15% reinforced, Standard |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2 |
| Flexural Modulus | 5650 | MPa | ISO 178 |
| Flexural Stress | 172 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.6 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 202 | °C | ISO 75-2/A |
| Linear thermal expansion coefficient | Internal method | ||
| Flow : 23 to 55°C | 4.0E-5 | cm/cm/°C | Internal method |
| Lateral : 23 to 55°C | 8.0E-5 | cm/cm/°C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Holding Pressure | 60.0 - 100 | MPa | |
| Screw Speed | 100 - 150 | rpm |
| Injection instructions |
|---|
| Cooling Time: Plasticization time + alpha or time without sticking in mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer T-500 | Shanghai Potomer International Trade Co., Ltd. | CPVC | Shanghai Potomer |
| Telcar® TL-2535F | Teknor Apex Company | TPE | Telcar® |
| Axiall PVC 3240 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| ESTOPLAST XU 6100BB03 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| LNP™ THERMOCOMP™ DF006 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |