TIPPLEN® H 543 F
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | MOL Petrochemicals Co. Ltd. |
| Trademark: | TIPPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9cNvZR_TIPPLEN-H-543-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TIPPLEN H 543 F is a homopolymer polypropylene with medium molecular weight, good mechanical properties and outstanding processability. This grade shows low water carry-over due to its special stabilization. TIPPLEN H 543 F is recommended for film yarns. Textiles film yarns with a denier count of not more than 1100 to 1200 are used for production of carpet backings, bags, industrial fabrics and mats. Yarns with a denier count of 3000 to 28000 are used for baler twines, packaging twines and ropes. TIPPLEN H 543 F is also recommended for cast and blown films, stiff sheets for thermoforming of cups, packaging of diary products and fruit-trays. TIPPLEN H 543 F is suitable for food contact. The product complies with Food Contact Regulations. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 1600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Injection Molded) | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 9.5 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C, Injection Molded) | 5.5 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 240 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Elastollan® 1190A10 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Karina BLACK PVC COMPOUND 850-48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MAJ'ECO EP300ALA | AD majoris | Biodeg Polymers | MAJ'ECO |
| Petrothene® NA340185 | LyondellBasell Industries | LDPE | Petrothene® |
| 3M™ Dyneon™ Fluoroelastomer FC 2122 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |