VALOX™ SHF4930 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9brus9_VALOX-SHF4930-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super high flow FR PBT grade with 15% Glass reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/2.16 kg | 18 | g/10 min | ASTM D1238 |
| 250°C/2.16 kg | 20 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 16.0 | cm³/10min | |
| 250°C/5.0 kg | 53.0 | cm³/10min | |
| Molding Shrinkage | Internal Method | ||
| Flow 1 | 0.50 to 0.80 | % | |
| Flow : 3.20 mm | 0.50 to 0.80 | % | |
| Across Flow 2 | 0.60 to 0.90 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.23 | % | |
| Equilibrium, 23°C, 50% RH | 0.070 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 190 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 6300 | MPa | ASTM D638 |
| -- | 6200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 80.0 | MPa | ASTM D638 |
| Yield | 85.0 | MPa | ISO 527-2/5 |
| Break 5 | 80.0 | MPa | ASTM D638 |
| Break | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 2.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Break 7 | 2.0 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 8 | 5170 | MPa | ASTM D790 |
| -- 9 | 5300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 140 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 129 | MPa | ASTM D790 |
| Flexural Strain at Break 11 | 3.0 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Filler Content | 15 | % | ASTM D229 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C | 6.0 | kJ/m² | ISO 179/2C |
| 23°C 12 | 6.0 | kJ/m² | ISO 179/1eA, ISO 179/2C |
| Charpy Unnotched Impact Strength | ISO 179/2U | ||
| -30°C | 23 | kJ/m² | |
| 23°C | 29 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 50 | J/m | ASTM D256 |
| 0°C | 50 | J/m | ASTM D256 |
| 23°C | 50 | J/m | ASTM D256 |
| -30°C 13 | 6.0 | kJ/m² | ISO 180/1A |
| 0°C 14 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 15 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| -30°C | 270 | J/m | ASTM D4812 |
| 23°C | 310 | J/m | ASTM D4812 |
| -30°C 16 | 19 | kJ/m² | ISO 180/1U |
| 23°C 17 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 55.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 215 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 18 | 215 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 195 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 19 | 195 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ASTM D1525 20 |
| -- | 197 | °C | ASTM D1525, ISO 306/B50 14 21 |
| -- | 218 | °C | ISO 306/A50 |
| -- | 195 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | |||
| Flow : -40 to 40°C | 3.9E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 9.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 9.8E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 0.800 mm, in Oil | 40 | kV/mm | |
| 1.50 mm, in Oil | 27 | kV/mm | |
| 1.60 mm, in Oil | 28 | kV/mm | |
| 3.20 mm, in Oil | 18 | kV/mm | |
| Dissipation Factor (1 MHz) | 0.016 | IEC 60250 | |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (0.750 to 1.50 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.800 mm | 750 | °C | |
| 1.50 mm | 700 | °C | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity | ISO 11443 | ||
| 250°C, 1500 sec^-1 | 90.0 | Pa·s | |
| 260°C, 1500 sec^-1 | 65.0 | Pa·s |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Tensile Bar |
| 3 . | 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 2 mm/min |
| 12 . | 80*10*4 sp=62mm |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 |
| 15 . | 80*10*4 |
| 16 . | 80*10*4 |
| 17 . | 80*10*4 |
| 18 . | 80*10*4 mm |
| 19 . | 80*10*4 mm |
| 20 . | Rate A (50°C/h), Loading 2 (50 N) |
| 21 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1001 GB 15 TFE 5 | RTP Company | PBT | RTP |
| ULTEM™ ATX200R resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |
| Chemical Resources GPPS1500 | Chemical Resources, Inc. | PS (GPPS) | Chemical Resources |
| FHR Polypropylene P5M4K-046 | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Karina BLACK PVC COMPOUND 806-48/ 1-H-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |