RAMOFIN PPC343T4
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9bGPqC_RAMOFIN-PPC343T4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% MINERAL FILLED, UV STABILIZED,HEAT STABILIZED POLYPROPYLENE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.4 | % | ASTM D955 |
| -- | 1.4 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 20.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 75 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 1200 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 30.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 125 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 69.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ASTM D1525, ISO 306 |
| Melting Temperature | 168 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 22 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 220 | °C | |
| Middle Temperature | 200 - 225 | °C | |
| Front Temperature | 205 - 230 | °C | |
| Mold Temperature | 30.0 - 65.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 461 | RTP Company | PS (HIPS) | RTP |
| Dryflex® A2 602600 | ELASTO | SEBS | Dryflex® |
| Durethan® BM 240 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Kingfa PA6-M25G20 | Kingfa | Nylon 6 | Kingfa |
| Iupilon® MB2112N | Mitsubishi Engineering-Plastics Corp | PC+Polyester | Iupilon® |