Kepamid® 2333GFH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9azvgY_Kepamid-2333GFH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KEPAMID 2333GFH is a 33% glass fiber reinforced and heat resistant polyamide-66. It exhibits good mechanical properties and long term heat resistance. It is applicable to automotive, electrical, electronic, and industrial parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.40 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 186 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9320 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 275 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 260 | °C | |
| 1.8 MPa, Unannealed | 255 | °C | |
| Melting Temperature | 260 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 260 to 300 | °C | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Nozzle Temperature | 260 to 300 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYREX® PH-88 | CHI MEI CORPORATION | PS (HIPS) | POLYREX® |
| VITAMIDE® BW34BK6358 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| ACRYPET® V | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| Fluon® ETFE | Asahi Glass Co., Ltd. | ETFE | Fluon® |
| CYCOLAC™ MG38F resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |