ForTii® XS51
| Category: | Nylon 4T , Polyamide 4T |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | ForTii® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9aiNYq_ForTiiXS51.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ForTii®XS51 is a Polyamide 4T (Nylon 4T) material, which contains a 40% glass fiber reinforced material. This product is available in the Asia-Pacific region,. ForTii®The main features of XS51 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.67 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.59 | -- | % | ISO 294-4 |
| Flow | 0.38 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 18500 | 18500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 230 | 210 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.3 | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 17000 | 17000 | MPa | ISO 178 |
| Flexural Stress | 350 | 310 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 90 | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 30 | -- | kV/mm | IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.40 mm | V-0 | -- | IEC 60695-11-10, -20 | |
| 1.5 mm | V-0 | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 325 - 335 | °C | |
| Front Temperature | 330 - 335 | °C | |
| Nozzle Temperature | 330 - 335 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 - 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PS 740 | Nexus Resin Group, LLC. | PS (HIPS) | NEXUS PS |
| Nypol® PA A3 G43 HS UV RH PRTA011 NR424 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Adell PE KR-18 | Adell Plastics, Inc. | HDPE | Adell PE |
| Durethan® BG 30 X FN01 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Elastron® G P.G401.A30.B | Elastron USA, Inc. | SEBS | Elastron® G |