POLYBEST 6 PD GF30 natural
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | POLYMA Kunststoff GmbH & Co. KG |
| Trademark: | POLYBEST |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9aH3Eg_POLYBEST-6-PD-GF30-natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYBEST 6 PD GF30 natural is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It can be processed by injection molding and is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.80 | -- | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.90 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 110 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | -- | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield | 170 | -- | MPa | |
| Break | 170 | -- | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Yield | 3.0 | -- | % | |
| Break | 3.0 | -- | % |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact Strength | 10 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 80 | -- | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 218 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 208 | -- | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 110 | -- | °C | |
| Vicat Softening Temperature | 220 | -- | °C | ISO 306/B |
| Ball Pressure Test (165°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature | 222 | -- | °C | DSC |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | > 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | without load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 6232 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| WPP PP PPC2CF7-Natural-UV | Washington Penn Plastic Co. Inc. | PP Copolymer | WPP PP |
| Chiao Fu PA66/6 MB312GM45 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| Huafon JF-A-AH5022 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| Karina IVORY PVC COMPOUND -E 500-35/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |