| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9YDPN9_VENYL-SFRH000R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SFRH000R is a halogen flame retardant compounds UL 94 V0 (conform 2002/95/EC, RoHS directive) polyamide 6 intended for injection moulding. APPLICATIONS VENYL SFRH000R has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. VENYL SFRH000R is available in black (VENYL SFRH000R-8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.80 to 1.3 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress 1 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 2.00 mm | 775 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 245 to 260 | °C | |
| Front Temperature | 245 to 260 | °C | |
| Nozzle Temperature | 225 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 75.0 to 95.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 to 65.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Note Message | |
|---|---|
| 1 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx FPP1A10CC | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Westlake HDPE MC3016 | Westlake Chemical Corporation | HDPE | Westlake HDPE |
| Pibiter® HI C3311 NERO900 | SO.F.TER. SPA | PBT | Pibiter® HI |
| Sylvin 9077-95LMW Grey 930 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8960-65FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |