HIPLEX® TR 144
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPLEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Tv66k_HIPLEX-TR-144.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPLEX® TR 144, copolymer of ethylene and hexene is tailored for blown film production. Extraordinary melt toughness made possible to get film down to 0.006 mm thickness. Extruded film has high impact resistance, good tear strength, excellent antiblock and good barrier properties, low gel content and excellent sealing and printing properties. Application: HIPLEX® TR-144 is suitable for production of composite films, carrier bags and other kinds of packaging. It is also recommended for blow moulding of small and medium size containers. HIPLEX® TR-144 has Health Certificate issued by Institute for Health Protection of Serbia. Also, HIPLEX® TR-144 has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.947 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.18 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (Condition B, F50) | > 1000 | hr | ISO 22088 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 21.0 | MPa | |
| Break | 32.0 | MPa | |
| Tensile Strain (Break) | 900 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm | 24.0 | MPa | |
| TD : Yield, 25 µm | 19.0 | MPa | |
| MD : Break, 25 µm | 40.0 | MPa | |
| TD : Break, 25 µm | 32.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 550 | % | |
| TD : Break, 25 µm | 690 | % | |
| Dart Drop Impact (25 µm) | 80 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25.0 µm | 27.0 | kN/m | |
| TD : 25.0 µm | 270.3 | kN/m |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Temperature 2 | 195 to 220 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 124 | °C | ISO 306 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blow-up ratio: 3.5-5 : 1, Neck height: 6-10 times die diameter |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPRO HDPE RH120 | Rondo Plast AB | HDPE | REPRO |
| TOTAL Polypropylene PPC 4944WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| YUPLENE® H730F | SK Global Chemical | PP Homopolymer | YUPLENE® |
| ENVIROPLAS® ENV12-NC120 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| Sylvin 6240-80 Red 6279 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |