ACRYLITE® L40 acrylic polymer is an amorphous thermoplastic molding compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® acrylic polymers are:

excellent weather resistance

high light transmission

high mechanical strength

high surface hardness and mar resistance

good melt flow rate

versatile colorability due to crystal clarity

The special properties of ACRYLITE® L40 polymer are:

low heat resistance

highest melt flow rate

UV light transmitting

medium levels of lubricant

Application:
Used for injection molding thin-wall medical devices requiring UV spectroscopy for fluid evaluation.

General Information
Additive	Lubricant
Features	Amorphous Good Colorability Good Flow Good Weather Resistance High Clarity High Hardness High Strength Lubricated Scratch Resistant
Uses	Medical/Healthcare Applications Thin-walled Parts
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.19	g/cm³	ASTM D792
Apparent Density	0.66	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	26	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.30 to 0.60	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	84		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3240	MPa	ASTM D638
Tensile Strength	60.7	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	2.0 to 4.0	%
Break	2.0 to 4.0	%
Flexural Modulus	3030	MPa	ASTM D790
Flexural Strength	97.9	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 6.35 mm)	19	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	74.0	°C	ASTM D648
Vicat Softening Temperature	82.0	°C	ASTM D1525
CLTE - Flow (0 to 156°C)	7.2E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	92.0	%	ASTM D1003
Haze (3200 µm)	< 1.0	%	ASTM D1003
Yellowness Index (3.20 mm)	< 1.0	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
Mowiflex™ FXT 305	Kuraray Co., Ltd.	PVOH	Mowiflex™
Multi-Pro® 3010 X	Multibase, A Dow Corning Company	PP, Unspecified	Multi-Pro®
LNP™ LUBRICOMP™ DCP32 compound	SABIC Innovative Plastics	PC	LNP™ LUBRICOMP™
Deprene 201-80	Shanghai Lin Gen Rubber Materials Co., Ltd.	PP+EPDM	Deprene
Edgetek™ Edgetek™ PC-20GF/000 FR BLK	PolyOne Corporation	PC	Edgetek™