RTP 103 CC HB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9SBYU9_RTP-103-CC-HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Chemically Coupled - UL94 HB |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4480 | MPa | ASTM D638 |
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.5 to 5.5 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 91 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 590 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 152 | °C | |
| 1.8 MPa, Unannealed | 143 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 1.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP513 | Kolon Plastics, Inc. | PBT | SPESIN® |
| VESTAMID® Care ML16 | Evonik Industries AG | Nylon 12 | VESTAMID® Care |
| UNITEM® Rg-30 | Nytef Plastics, Ltd. | PEI | UNITEM® |
| Fainplast PVC PHS 75/B | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| KOPLA PA6 KNG1020F | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |