ULTEM™ CRS5001 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9RIQCT_ULTEMCRS5001resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent, Standard flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones.Resin is RoHS compliant. UL94 V0 listing. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.60 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.2 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 135 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 100 | MPa | ISO 527-2/50 |
| Fracture | 95.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 8.0 | % | ISO 527-2/50 |
| Fracture | 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2500 | MPa | ISO 178 |
| Flexural Stress 3 | ISO 178 | ||
| -- 4 | 105 | MPa | ISO 178 |
| -- 5 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6 | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 100 mm span | 210 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 200 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 225 | °C | ISO 306/A50 |
| -- | 220 | °C | ISO 306/B50 |
| -- | 222 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.29 | W/m/K | ISO 8302 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 1.60mm, in oil | 26 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.20 | IEC 60250 | |
| 60 Hz | 3.20 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.6E-3 | IEC 60250 | |
| 60 Hz | 1.6E-3 | IEC 60250 | |
| 1 MHz | 4.3E-3 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 175 | V | IEC 60112 |
| Solution B | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 47 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 325 - 365 | °C | |
| Middle Temperature | 350 - 390 | °C | |
| Front Temperature | 370 - 410 | °C | |
| Nozzle Temperature | 360 - 400 | °C | |
| Processing (Melt) Temp | 360 - 410 | °C | |
| Mold Temperature | 120 - 170 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | Break |
| 5 . | Yield |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOPLA® KE101 | Kolon Plastics, Inc. | PEN+PET | NOPLA® |
| BJB Polyurethane SC-115 | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| DOMAMID® 6G50HCE | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Eastar™ MN005 | Eastman Chemical Company | Copolyester | Eastar™ |
| GLAMIDE® NB-5550 | TOYOBO America, Inc. | Nylon, Unspecified | GLAMIDE® |