Di-Pak™ E-4650
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9R6yTk_Di-Pak-E-4650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DI-PAK E-4600 SERIES Flexible, high strength, 50 to 71 shore D hardness potting and encapsulating systems. Available in flame retardant (FR), 3 minute (-3) gel time, and in black or unpigmented. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Weight - per cubic inch | 17 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 125 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 25.0 | min | ASTM D2971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Shock Test | Pass |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 47 to 50 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 131 | MPa | ASTM D638 |
| Tensile Strength | 12.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 280 | % | ASTM D638 |
| Flexural Modulus | 80.7 | MPa | ASTM D790 |
| Flexural Strength | 5.79 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 2 | 62.3 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 75 | J/m | ASTM D256 |
| Unnotched Izod Impact | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.22 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.4E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | > 14 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 3.10 | ||
| 100 kHz | 2.90 | ||
| Dissipation Factor (25°C, 100 kHz) | 0.031 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 85, Mix Ratio by Volume: 80 | ||
| Thermoset Mix Viscosity (25°C) | 870 | cP | ASTM D4878 |
| Demold Time (21°C) | 120 to 300 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| 2 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| TOTAL Polypropylene PPC 11812 S01 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Nordbak Castable Wear Compound | Loctite® | Epoxy | Nordbak |
| Karina BLACK PVC COMPOUND 600D48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Starex LX-0760 | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |