CONATHANE® EN-1556
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Cytec Industries Inc. |
| Trademark: | CONATHANE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9MGOLe_CONATHANE-EN-1556.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CONATHANE EN-1556 is a polyether based, non-MBOCA polyurethane resin system primarily intended for use as a molding, encapsulating, and potting compound for harness breakouts, Watertight electrical connectors, cables, cable end seals, printed circuitry, and other electrical components. The system also has use in the casting or molding of mechanical parts and as a lining material for pumps, chutes, and conveyors Where outstanding abrasion resistance is a necessity. CONATHANE EN-1556 may be cured at room or elevated temperatures. CONATHANE EN-1556, When fully cured, is a tough, cold-flow resistant elastomer that has good resistance to oils, gasoline, JP-4 fuel, Water, and sea Water and also provides outstanding protection against corrosion or contamination. The system is funginert When tested in accordance With MIL-I-46058C and ASTM G-21 and meets or exceeds all of the requirements of MIL-M-24041 C. Three primers have been developed for use in bonding CONATHANE EN-1556 to metals, neoprene, and polyvinyl chloride during the curing process. CONAP® AD-1146 is recommended for metals, CONAP® PR-1167 for neoprene, and CONAP® AD-1 161 for polyvinyl chloride. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.03 | g/cm³ | |
| -- 2 | 1.05 | g/cm³ | |
| Water Absorption - 24 hour immersion in D.I. water @ 200°F | 0.33 | % | |
| Shrinkage - Volume | 3.6 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Fungal Resistance | Non-nutrient | ||
| Isocyanate Content 3 | 5.2 | % | |
| Non-Volatile Content - Mixed System | 100 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 300% Secant | 9.65 | MPa | Internal Method |
| Tensile Strength | 34.5 | MPa | |
| Tensile Elongation (Break) | 400 | % |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 4 | 35.0 | kN/m | |
| Compression Set (70°C, 22 hr) | 35 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- 5 | 3.5E+10 | ohms | |
| -- 6 | 5.2E+13 | ohms | |
| Volume Resistivity | |||
| 25°C | 2.4E+12 | ohms·cm | |
| 121°C | 9.6E+10 | ohms·cm | |
| Dielectric Strength (3.18 mm) | 14 | kV/mm | |
| Dielectric Constant | ASTM D150 | ||
| 25°C, 1 kHz | 6.12 | ||
| 25°C, 1 MHz | 5.06 | ||
| Arc Resistance | > 120 | sec | |
| Insulation Resistance | |||
| 25°C | 9.0E+11 | ohms | |
| 121°C | 4.2E+9 | ohms |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 33 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Thermoset Mix Viscosity | |||
| 25°C 7 | 3000 | cP | |
| 25°C 8 | 18000 | cP |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mix |
| 3 . | Resin |
| 4 . | Die C |
| 5 . | 250°F |
| 6 . | 77°F |
| 7 . | Hardener |
| 8 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6003-75A | RTP Company | TPE | RTP |
| PROTEQ™ L24C4 | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| ULTEM™ 2210EPR resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Enviramid® N2340MGHL BK | Ravago Manufacturing Americas, LLC | Nylon 6 | Enviramid® |
| PLUSTEK RA320G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |