Kingfa PET-G30
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9M0TLy_Kingfa-PET-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PET-G30 is a polyethylene terephthalate (PET) material, which contains a 30% glass fiber reinforced material. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PET-G30 are:
The typical application field of Kingfa PET-G30 is: automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.30 | % | ASTM D955 |
| Transverse flow : 23°C | 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 145 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus 3 | 9500 | MPa | ASTM D790 |
| Flexural Strength 4 | 205 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 85 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 240 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 230 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 235 - 255 | °C | |
| Middle Temperature | 245 - 265 | °C | |
| Front Temperature | 255 - 275 | °C | |
| Processing (Melt) Temp | 255 - 275 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temperature Limit: 270°C |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Glastic® 1461 | Glastic Corporation | Polyester, TS | Glastic® |
| Hifax CA45G | LyondellBasell Industries | TPO (POE) | Hifax |
| Kareline® PLMS7525 | Plasthill Oy | PLA | Kareline® |
| POLYfill PPH GF12030 PD2 | Polykemi AB | PP Homopolymer | POLYfill |
| KMI PP KM-058IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |