TRIBOCOMP® PC GF30 TS0
| Category: | PC , Polycarbonate |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Lb89L_TRIBOCOMP-PC-GF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP®PC GF30 TS0 is a polycarbonate (PC) product, which contains 15% ptfe fiber and 30% glass fiber reinforced materials. It is available in Europe. The main characteristics are: lubrication. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | ||
| 23°C | 9600 | MPa | ISO 527-2 |
| 90°C | 8700 | MPa | ISO 527-2 |
| 120°C | 8000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 115 | MPa | ISO 527-2 |
| Fracture, 90°C | 80.0 | MPa | ISO 527-2 |
| Fracture, 120°C | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 8100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 135 | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.5E-5 | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.29 | W/m/K | ISO 22007 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 36 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Additional Information |
|---|
| The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 300 | °C | |
| Middle Temperature | 270 - 320 | °C | |
| Front Temperature | 275 - 320 | °C | |
| Nozzle Temperature | 275 - 320 | °C | |
| Processing (Melt) Temp | < 330 | °C | |
| Mold Temperature | 90.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AT0620GB | Ginar Technology Co., LTD. | Nylon 66 | Mapex |
| Sinvicomp DBS5906 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| TOYOBO Urethane A1064D | TOYOBO America, Inc. | PUR-Butyl | TOYOBO Urethane |
| Topolymer® 5111-951E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| DESLON™ 6 DSC101STA | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |