Developmental DTF1602.00 ESU
| Category: | TPO , Developmental Performance Polymers |
| Manufacturer: | Trinseo |
| Trademark: | Developmental |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9I5pn6_Developmental-DTF1602-00-ESU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DTF1602.00 ESU Developmental PP Compound exhibits good processing, good impact and high stiffness performance. In addition, this grade offers low gloss, good UV stability and scratch/abrasion resistance. In combination with a density of 1.01, which is lower than the industry standard, this grade allows reducing the weight of parts. This unique set of performance characteristics makes it a suitable product for many complex, unpainted and uncovered applications in the car interior, whether the part is subject to high temperatures and direct sunlight, or is located in highly visible and scratch sensitive areas. Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.3 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 30 | % | ISO 527-2/50 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | ISO 180/1A |
| 23°C | 9.0 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy 1(0°C, 2.00 mm) | 12.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 64.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 140 | °C | ISO 306/A120 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 2(1.00 mm) | 45 | mm/min | ISO 3795 |
| Additional Information |
|---|
| Testing performed on injection moulded samples in natural. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 260 | °C | |
| Mold Temperature | 20.0 - 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Energy to Break |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SA102-HL | RJM International, Inc. | PC | RJM |
| APEX® RE 9018 | Teknor Apex Company | PVC, Rigid | APEX® |
| Eltex® P HV001PF | INEOS Olefins & Polymers Europe | PP Homopolymer | Eltex® P |
| LUVOCOM® PEEK CLASSIX 7994 VP | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Geon™ Vinyl Dry Blend EP680 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Dry Blend |