LNP™ COLORCOMP™ 144C compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9HfqQv_LNPCOLORCOMP144Ccompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* COLORCOMP* 144C is a compound based on Polycarbonate. Added features of this grade include: UL rated HB, 200 series recommended when V-2 rating required, 10.5 MFR, FDA food contact compliant in limited colors. Effective January 15, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183, ASTM D792 |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | |||
| 24 hr | 0.15 | % | ASTM D570 |
| Saturated, 23°C | 0.26 | % | ISO 62 |
| Equilibrium, 23°C | 0.35 | % | ASTM D570 |
| Equilibrium, 100°C | 0.58 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 70 | ASTM D785 | |
| Class r | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2390 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 68.0 | MPa | ASTM D638 |
| Fracture | 73.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 130 | % | ASTM D638 |
| Fracture | 130 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2340 | MPa | ASTM D790 |
| -- | 2250 | MPa | ISO 178 |
| -- 7 | 2250 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 93.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 96.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 9(23°C) | 82 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 220 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 10 | 10 | kJ/m² | ISO 180/1A |
| 23°C 11 | 71 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 88.0 | J | ASTM D3763 |
| Dart Drop Impact (23°C) | 169 | J | ASTM D3029 |
| Tensile Impact Strength 12 | 577 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 126 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 132 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 127 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ASTM D1525 14 |
| -- | 143 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 95°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1250 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.17 | ASTM D150 | |
| 60 Hz | 3.17 | ASTM D150 | |
| 1 MHz | 2.96 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ASTM D150 | |
| 60 Hz | 9.0E-4 | ASTM D150 | |
| 1 MHz | 0.010 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.5 mm) | HB | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 271 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 293 - 316 | °C | |
| Nozzle Temperature | 288 - 310 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 71 - 93 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | Type S |
| 13 . | 120*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 9659 | Chevron Phillips Chemical Company LLC | HDPE | MarFlex® |
| Purell RP373R | LyondellBasell Industries | PP Random Copolymer | Purell |
| Weifang Kingdom CPVC | Weifang Kingdom Plastic Co., Ltd | CPVC | Weifang Kingdom |
| Fainplast PVC PM 5526/1 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| PENTAMID AB E5 H schwarz | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |