Order Products : sales@su-jiao.com
SNOLEN® EP 0.49/47
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | JSC Gazprom neftekhim Salavat |
| Trademark: | SNOLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9Glvzz_SNOLEN-EP-0-49-47.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CHARACTERISTIC PROPERTIES Extra-high environmental stress crack resistance. High impact strength. UV protection not required. MAJOR APPLICATIONS PE 80 Pipe Grades: process pipes, incl. pressure pipes; gas pipes; potable water pipes; unpressurized pipes; wear plates; fittings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.943 to 0.947 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/21.6 kg | 8.0 to 16 | g/10 min | |
| 190°C/5.0 kg | 0.41 to 0.49 | g/10 min | |
| Environmental Stress-Cracking Resistance 1(80°C, 2% Arkopal) | 50.0 | hr | ISO 16770 |
| Melt Flow Ratio | 23.0 to 31.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resistance to Rapid Crack Propagation, Pc - Test S4 | > 3.00 | bar | ISO 13477 |
| Resistance to Slow Crack Growth - Notch Test (SCG) 2 | > 250 | hr | ISO 13479 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Resistance to Internal Pressure - Hydrostatic Strength 3(80°C) | > 1.4 | month | ISO 1167 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 850 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 22.0 | MPa | |
| Break | 35.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 8.0 | % | |
| Break | > 850 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 23 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 67.0 | °C | ISO 306/B50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | @ 4.0 MPa |
| 2 . | @ 4.0 MPa |
| 3 . | @ 4.6 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prop 6003 | Putsch Kunststoffe GmbH | PP, Unspecified | Prop |
| Shuman PC 930 | Shuman Plastics, Inc. | PC | Shuman PC |
| NYCOA Polyamide 5033 HST | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| ESTASTIR HI 0508 V0 | Cossa Polimeri S.r.l. | PS (HIPS) | ESTASTIR |
| Durethan® BKV 30 EF 000000 | LANXESS GmbH | Nylon 6 | Durethan® |