Pebax® Rnew 25R53 SP 01
| Category: | PEBA-Ether , Polyether Block Amide |
| Manufacturer: | Arkema |
| Trademark: | Pebax® Rnew |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9GcS0M_Pebax-Rnew-25R53-SP-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyether block amide Pebax® Rnew 25R53 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 26 | ||
| Shore D, 15 sec | 22 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 34.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 750 | % | ISO 527-2 |
| Flexural Modulus | 20.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 62.0 | °C | ISO 306/A |
| Melting Temperature | 136 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 17 to 21 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 55.0 to 65.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 180 to 240 | °C | |
| Mold Temperature | 10.0 to 30.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 55.0 to 65.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 170 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000 Compression Molded Shape | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| Unilex™ UP.700.935U | United Polychem | PE, Unspecified | Unilex™ |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6105 BR | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Desmovit® DP R 3926 | geba Kunststoffcompounds GmbH | TPU-Ester/Ether | Desmovit® |
| ENGAGE™ 8540 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |