Lion Idemitsu Composites PPS V170N3
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Lion Idemitsu Composites Co., Ltd. |
| Trademark: | Lion Idemitsu Composites PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9G4w2G_Lion-Idemitsu-Composites-PPS-V170N3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lion Idemitsu Composites PPS V170N3 is a Polyphenylene Sulfide (PPS) product. It is available in Asia Pacific. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.74 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.50 | % | |
| Flow | 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.16 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 45 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 21.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.70 | % | ISO 527-2 |
| Flexural Modulus | 6300 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 1.1 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 132 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 2.1E-5 | cm/cm/°C | |
| Transverse | 2.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Electric Strength (3.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 3.90 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (4.50 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flowability 2(1.00 mm) | 150 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | Internal Method |
| 2 . | Thickness 1mm, Cylinder temperature 320°C, Injection pressure 100MPa, Mold temperature 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Neostar™ FN005 | Eastman Chemical Company | Copolyester Elastomer (Ether) | Neostar™ |
| Anjacom® 036/80 | Almaak International GmbH | Nylon 6+ASA | Anjacom® |
| ASI POLYPROPYLENE 1259 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Eporex® 827 | Eternal Plastics Co., Ltd. | PS (HIPS) | Eporex® |
| Karina CLEAR PVC COMPOUND -E 84/203-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |