AEI TP519C

Category:	PE, Unspecified , Polyethylene
Manufacturer:	AEI Compounds Limited
Trademark:	AEI
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	9FwXif_AEI-TP519C.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Thermoplastic, low-smoke, halogen-free flame retardant compound for data and communication cable.

This is a flame-retardant low-smoke thermoplastic compound, which has been specially developed to meet the requirements of limited toxic and corrosive fume emission. TP519C has been developed to offer good processability at high extrusion speeds and has very little die drool.

TP519C is available in the following versions:

TP519C (natural colour)

TP519CB (coloured black)

TP519CU (with a non-staining UV stabiliser added)

TP519CBU (carbon black added to give UV stability)

General Information
Additive	Flame retardancy
Features	Low smoke Workability, good Halogen-free Flame retardancy
Uses	Communication Cable Jacketing Flame Retardant Jacketing Wire and cable applications
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Forms	Particle
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density	1.50	g/cm³	BS 2782 620A
Melt Mass-Flow Rate (MFR) (150°C/21.6 kg)	14	g/10 min	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	90

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	13.0	MPa	IEC 60811-1-1
Tensile Strain
Fracture	140	%	IEC 60811-1-1
Fracture, -30°C ¹	50	%	IEC 60811-1-4

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength
50°C, 336 hr, in Hydrochloric Acid, 1N	17	%
50°C, 336 hr, in Sodium Hydroxide, 1N	45	%
70°C, 4 hr, in ASTM #2 oil	18	%
135°C, 168 hr	12	%	IEC 60811-1-2
Change in Tensile Strain at Break
50°C, 336 hr, in Hydrochloric Acid, 1N	14	%
50°C, 336 hr, in Sodium Hydroxide, 1N	20	%
70°C, 4 hr, in ASTM #2 oil	7.0	%
135°C, 168 hr	-10	%	IEC 60811-1-2

Thermal	Nominal Value	Unit	Test Method
Deformation (80°C)	15	%	IEC 60811-3-1
Cold shock (-30°C)	pass		IEC 60811-1-4
Cold bending (-30°C)	pass		IEC 60811-1-4
Temperature index	270	°C	ISO 4589-3

Electrical	Nominal Value	Unit	Test Method
Insulation Constant - Ki			IEC 60502
20°C	9.5E+10	ohms·cm	IEC 60502
90°C	6.5E+7	ohms·cm	IEC 60502

Flammability	Nominal Value	Unit	Test Method
Smoke- 3m cube test	pass		EN 61034

Additional Information	Nominal Value	Unit	Test Method
Halogen Acid Gas Evolution		%	IEC 60754-2
Tear Strength	5	N/mm	BS 6469

Extrusion	Nominal Value	Unit
Head Temperature	155	°C

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity (20°C)	2.0E+14	ohms·cm	IEC 60502
Dielectric Strength (20°C)	19	kV/mm	IEC 60243-1
Relative Permittivity (23°C, 50 Hz)	4.65		IEC 60250

Flammability	Nominal Value	Unit	Test Method
Oxygen Index	31	%	ISO 4589-2

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	115	°C
Cylinder Zone 2 Temp.	125	°C
Cylinder Zone 3 Temp.	135	°C
Cylinder Zone 4 Temp.	145	°C
Melt Temperature	< 170	°C
Die Temperature	160	°C

Extrusion instructions
An extruder with an L/D ratio (length/diameter) of 15-24 and an extruder screw with a compression ratio 1.2:1 to 2.5:1 are recommended.

Note Message
1 .	pass

Resin Grade	Manufacturer	Category	Trademark
RTP 985	RTP Company	PSU	RTP
Milastomer™ 5517BS	Mitsui Chemicals America, Inc.	TPV	Milastomer™
NuSil R-2145	NuSil Technology	Silicone	NuSil
Altuglas® VM 100	Altuglas International of Arkema Inc.	Acrylic (PMMA)	Altuglas®
Optix® CP-927	Plaskolite West, Inc.	Acrylic (PMMA)	Optix®