NPC PE LL0209AF
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NPC Alliance Corporation |
| Trademark: | NPC PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9FuzLn_NPC-PE-LL0209AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL0209AF is a linear low-density polyethylene copolymer with Butene-1 as the comonomer. It is intended for wide range of blown film applications, which offers superior hot-tack performance and higher tensile strength. LL0209AF contains process aid to allow easier extrusion; thus, preventing melt fracture. APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 38 µm | 11.0 | MPa | |
| TD : Yield, 38 µm | 12.0 | MPa | |
| MD : Break, 38 µm | 40.0 | MPa | |
| TD : Break, 38 µm | 31.0 | MPa | |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 38 µm | 650 | % | |
| TD : Break, 38 µm | 850 | % | |
| Dart Drop Impact (38 µm) | 160 | g | ISO 6603-2 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 38 µm | 2.4 | N | |
| TD : 38 µm | 6.0 | N |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 122 | °C | ASTM D2117 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm) | 50 | ASTM D2457 | |
| Haze (38.0 µm) | 12 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® RJ6428 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Random Copolymer | POLYPRO® |
| TechnoFin TV 40 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |
| Karina MBPEB ANTISPLIT - 1000/0080 IE | Karina Ind. e Com. de Plásticos Ltda | LDPE | Karina |
| Panlite® MN-4800Z | TEIJIN LIMITED | PC | Panlite® |
| ULTEM™ HU1000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |