Nylene® 607

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Custom Resins Group
Trademark:	Nylene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	9FPOZg_Nylene-607.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Very high viscosity extrusion resin having an ASTM relative viscosity of 800

Excellent structural strength, durability, and physical properties

Good melt strength and good draw-down properties which promote dimensional control for extrusion of pipe, tubing, film, and sheet

Particularly recommended for the extrusion of thick slab, large rod stock, and large complex profiles

Optimum processing conditions should permit for a melt temperature of 550 - 575°F at the die.

General Information
Features	Durable Good Strength Ultra High Viscosity
Uses	Film Piping Pressed Slabs Profiles Rods Sheet Tubing
Processing Method	Extrusion Pipe Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.14	g/cm³	ASTM D792

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	84.8	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	210	%	ASTM D638

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	48	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, Unannealed	186	°C
1.8 MPa, Unannealed	65.0	°C

Extrusion	Nominal Value	Unit
Melt Temperature	288 to 302	°C

Resin Grade	Manufacturer	Category	Trademark
Sindustris ABS LEF489P	Sincerity Australia Pty Ltd.	ABS	Sindustris ABS
Novalloy-B B5526	PlastxWorld Inc.	ABS+PBT	Novalloy-B
EL-Pro™ P607F	SCG Chemicals Co., Ltd.	PP Homopolymer	EL-Pro™
LNP™ THERMOCOMP™ OC006 compound	SABIC Innovative Plastics	PPS, Linear	LNP™ THERMOCOMP™
POCAN® B 5220 XF 000000	LANXESS GmbH	PBT	POCAN®