ULTEM™ AR9200 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9EWdbn_ULTEM-AR9200-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 5.7 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.50 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6960 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 152 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 7240 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 207 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (3.20 mm) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 211 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| FAA Flammability 6 | NATURAL | FAR 25.853 | |
| NBS Smoke Density | ASTM E662 | ||
| Flaming, Dmax | 5.00 | ||
| Flaming, Ds, 1.5 min | 0.00 | ||
| Flaming, Ds, 4 min | 5.00 | ||
| OSU Peak Heat Release Rate 7 | 40.0 | kW/m² | FAR 25.853 |
| OSU Total Heat Release 8 | 5.00 | kW·min/m² | FAR 25.853 |
| Vertical Burn Test | FAR 25.853 | ||
| Test a (60 s), passes at | 0.0 | hr | |
| Test b (12 s), passes at | 0.0 | hr |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 343 to 366 | °C | |
| Middle Temperature | 354 to 377 | °C | |
| Front Temperature | 366 to 388 | °C | |
| Nozzle Temperature | 360 to 382 | °C | |
| Processing (Melt) Temp | 366 to 388 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Method A/B |
| 7 . | 5 minute test |
| 8 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen D50G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| TEREZ PA 6.6 7750 TC | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Karina BLUE PVC COMPOUND 810-06/115-CRB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND 105900-35/ 1-B-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SABIC® PPcompound 8650U | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |