NANCAR® 1031
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9DstcR_NANCAR-1031.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 1031 is a high acrylonitrile butadiene copolymer with excellent oil, fuel, grease, water and steam resistance. It is polymerized at low temperature and contains sufficient antioxidant for normal aging conditions. NANCAR® 1031 is recommended for use in high oil resistant rubber parts with low metal corrosion and high water resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | |
| Mooney Viscosity | ASTM D1646 | ||
| ML 1+4, 100°C 1 | 79 | MU | |
| ML 1+4, 100°C | 63 | MU | |
| Acrylonitrile Content - Bound | 41.0 | % | Internal Method |
| Solubility - in MEK | 100 | % | |
| Stabilizer | Non-staining | ||
| Viscosity | ASTM D1646 | ||
| Minimum | 46.0 | ||
| Minutes to 35 points rise, t35 | 43.6 | min | |
| Minutes to 5 points rise, t5 | 33.7 | min |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.40 | % | ASTM D5688 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 5 sec 2 | 77 | ||
| Shore A, 5 sec 3 | 76 | ||
| Shore A, 5 sec 4 | 75 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 300% Strain 5 | 12.3 | MPa | |
| 300% Strain 6 | 10.7 | MPa | |
| 300% Strain 7 | 7.94 | MPa | |
| Tensile Strength | ASTM D412 | ||
| Yield 8 | 26.9 | MPa | |
| Yield 9 | 26.3 | MPa | |
| Yield 10 | 24.4 | MPa | |
| Tensile Elongation | ASTM D412 | ||
| Break 11 | 580 | % | |
| Break 12 | 630 | % | |
| Break 13 | 770 | % | |
| Tear Strength | 65.7 | kN/m | ASTM D624 |
| Compression Set 14(100°C, 70 hr) | 74 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 15(100°C, 70 hr) | 1.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air 16(100°C, 70 hr) | -30 | % | ASTM D573 |
| Change in Durometer Hardness in Air 17(Shore A, 100°C, 70 hr) | 5.0 | ASTM D573 | |
| Change in Tensile Strength 18 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | 3.0 | % | |
| 100°C, 70 hr, in IRM 903 Oil | -5.0 | % | |
| Change in Ultimate Elongation 19 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -27 | % | |
| 100°C, 70 hr, in IRM 903 Oil | -18 | % | |
| Change in Durometer Hardness 20 | ASTM D471 | ||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | 4.0 | ||
| Shore A, 100°C, 70 hr, in IRM 903 Oil | -6.0 | ||
| Change in Volume 21 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM Oil #1 | -0.30 | % | |
| 100°C, 70 hr, in IRM 903 Oil | 11 | % |
| Note Message | |
|---|---|
| 1 . | Uncured |
| 2 . | CURED @150°C for 60 mins |
| 3 . | CURED @150°C for 40 mins |
| 4 . | CURED @150°C for 20 mins |
| 5 . | CURED @150°C for 60 mins |
| 6 . | CURED @150°C for 40 mins |
| 7 . | CURED @150°C for 20 mins |
| 8 . | CURED @150°C for 60 mins |
| 9 . | CURED @150°C for 40 mins |
| 10 . | CURED @150°C for 20 mins |
| 11 . | CURED @150°C for 60 mins |
| 12 . | CURED @150°C for 40 mins |
| 13 . | CURED @150°C for 20 mins |
| 14 . | CURED @150°C for 60 mins |
| 15 . | CURED@150°C × 40 MINUTES |
| 16 . | CURED@150°C × 40 MINUTES |
| 17 . | CURED@150°C × 40 MINUTES |
| 18 . | CURED@150°C × 40 MINUTES |
| 19 . | CURED@150°C × 40 MINUTES |
| 20 . | CURED@150°C × 40 MINUTES |
| 21 . | CURED@150°C × 40 MINUTES |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PL-1131 | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| NOVA PC 1043 C2 | NOVA Polymers, Inc. | PC | NOVA PC |
| Evermore PUR SA-2021MP | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| KOCETAL® SO301 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| LEXAN™ CFR5630D resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |