PROTEQ™ C12US
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | PROTEQ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9BX9hD_PROTEQ-C12US.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PROTEQ™ C12US is a medium flow polypropylene copolymer with good impact properties. The grade has been UV and heat stabilised for applications requiring resistance to degradation caused by harmful UV radiations and long term heat exposure. The base resin and all additives used in the compound have relevant approvals for use in food contact applications according to the existing documentation provided by their suppliers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 70 | ||
| Shore D, 15 sec | 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 50 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 850 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 37.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 100 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 52.0 | °C | ASTM D648 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 195 to 215 | °C | |
| Middle Temperature | 205 to 225 | °C | |
| Front Temperature | 215 to 235 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP LDPE 023919 | Amco Polymers | LDPE | PRIMATOP |
| Teslin® SP 600 | PPG Industries, Inc. | PE, Unspecified | Teslin® |
| CALP E4362K | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| LG ABS RS650 | LG Chem Ltd. | ABS | LG ABS |
| LNP™ THERMOCOMP™ PX01658 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |