NORYL™ PX0844 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9BQENM_NORYLPX0844resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL PX0844 is an unfilled standard material with a Vicat B/120 of 125°C according ISO306. NORYL PX0844 offers high heat resistance and consistant processability. Typical |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/3.8 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.14 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Fracture | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.0 | % | ISO 527-2/50 |
| Fracture | 40 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2200 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3 | ISO 180/1A | ||
| -40°C | 5.0 | kJ/m² | ISO 180/1A |
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 100 mm span | 115 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 105 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 123 | °C | ISO 306/B50 |
| -- | 125 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF12 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Ebalta AH 100 / TGL | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Ebalta GM 956 / GM 956-1 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Electrafil® J-1200/CF/20 NAT | Techmer Engineered Solutions | ABS | Electrafil® |
| Durethan® BM 240 000000 | LANXESS GmbH | Nylon 6 | Durethan® |