Ultramid® 8202 L
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9AynOt_Ultramid-8202-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8202 L is an unreinforced, low viscosity, highly lubricated PA6 injection molding homopolymer exhibiting excellent melt fluidity for filling thin sections. Applications Ultramid 8202 L is generally recommended for applications such as: gears, fittings, casters, bearings, clips, fasteners, plugs, caps, and filter bowls. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.13 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.2 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.6 | -- | % | |
| Saturation | 9.5 | -- | % | |
| Equilibrium, 50% RH | 2.7 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 125 | 110 | MPa | |
| Yield, 23°C | 79.0 | 36.0 | MPa | |
| Yield, 80°C | 35.0 | 30.0 | MPa | |
| Yield, 121°C | 25.0 | 21.0 | MPa | |
| Break, 23°C | 75.0 | 60.0 | MPa | |
| Tensile Elongation | ASTM D638 | |||
| Yield, 23°C | 4.0 | 16 | % | |
| Yield, 80°C | 42 | 35 | % | |
| Yield, 121°C | 36 | 40 | % | |
| Break, 23°C | 55 | > 100 | % | |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 3010 | 3660 | MPa | |
| 23°C | 2830 | 740 | MPa | |
| 65°C | 500 | -- | MPa | |
| 90°C | 350 | -- | MPa | |
| 121°C | 305 | -- | MPa | |
| Flexural Strength | ASTM D790 | |||
| -40°C | 170 | 155 | MPa | |
| 23°C | 110 | 35.0 | MPa | |
| 65°C | 30.0 | -- | MPa | |
| 90°C | 20.0 | -- | MPa | |
| 121°C | 20.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 50 | 45 | J/m | |
| 23°C | 60 J/m | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 178 | -- | °C | |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418 |
| CLTE - Flow | 8.3E-5 | -- | cm/cm/°C | ASTM E831 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 240 to 285 | °C | |
| Mold Temperature | 65.0 to 80.0 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5930 | Spartech Polycom | PP, Unspecified | Spartech |
| Daelim Po1y® 50100F | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Eleme HFG00356 | Eleme Petrochemical Company Ltd | HDPE | Eleme |
| Karina IVORY PVC COMPOUND -E 602D35/ 1-A-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TAFMER™ MH7010 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |