Geon™ HTX M6309
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9AcV6O_Geon-HTX-M6309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™ HTX M6309 is a Polyvinyl Chloride Alloy (PVC Alloy) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Geon™ HTX M6309 include outdoor applications, construction applications, electrical/electronic applications and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Spiral Flow | 63.5 | cm | |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Outdoor Suitability (Gray) | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1650 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 29.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 56 | % | ASTM D638 |
| Flexural Modulus | 1650 | MPa | ASTM D790 |
| Flexural Strength | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| -40°C, 3.18 mm, Injection Molded | 210 | J/m | |
| -18°C, 3.18 mm, Injection Molded | 590 | J/m | |
| 0°C, 3.18 mm, Injection Molded | 750 | J/m | |
| 23°C, 3.18 mm, Injection Molded | 850 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 75.0 | °C | |
| 0.45 MPa, Annealed, 6.35 mm | 83.9 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 67.8 | °C | |
| 1.8 MPa, Annealed, 6.35 mm | 73.9 | °C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.01 mm, ALL | V-0 | ||
| 3.00 mm, ALL | 5VA |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| QUV Weatherometer 4 | 0.50 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 68.3 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 202 to 207 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 51 mm/min |
| 4 . | 351 Lamp, All Colors, detla E (CIE), 24 hrs light, 300 hrs, No Moisutre |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® R533T | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Alpha PVC 7731 NATURAL | AlphaGary | PVC, Unspecified | Alpha PVC |
| Fiberfil® J-60/30/E/M | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Integra™ PBT-4123 | PolySource, LLC | PBT | Integra™ |
| Durethan® A 30 S FN31 000000 | LANXESS Asia/Pacific | Nylon 66 | Durethan® |